Automotive

The automotive sector is facing increasingly strict requirements regarding fuel efficiency and weight reduction. All these requirements have to be met without compromising safety, performance and processing efficiency. Tepex® provides material solutions for structural and semi-structural parts that bridge such apparent contradictions of weight reduction, structural performance and maximum energy absorption.

Low processing cycle-times of Tepex® material systems enable cost efficient parts and reliable mass-production processes in the automotive industry.

Major challenges in the automotive industry can be addressed with Tepex® material solutions:

  • Weight reduction
  • Safety
  • Energy absorption
  • Process efficiency
  • Mass production ability

The following menu shows standard Tepex® materials for Automotive applications. Custom made material lay-ups as well as special fabric constructions will be available on request.

Glass/PA66

Tepex® dynalite 101-RG600(x)/47% black

Polymer:

PA6.6 black

Fiber RG600:

E-glass, 1200 tex

Weaving RG600:

600 g/m² area weight

Twill 2/2 binding

Warp 0° -> 50% fibers

Weft 90° -> 50% fibers

Lay-up:

RG600 -> (x) = number of layers

(max. 8 layers = 4.0mm thickness)

Fibervolumecontent:

47% vol.

 

Tepex® dynalite 101-RG601(x)/47% black

Polymer:

PA6.6 black

Fiber RG601:

E-glass, 1200 tex

Weaving RG601:

600 g/m² area weight

Plain weave

Warp 0° -> 50% fibers

Weft 90° -> 50% fibers

Lay-up:

RG601 -> (x) = number of layers

(max. 8 layers = 4.0mm thickness)

Fibervolumecontent:

47% vol.

 

Tepex® dynalite 101-RGUD600(x)/47% black

Polymer:

PA6.6 black

Fiber RGUD600:

E-glass, 1200 tex

Weaving RGUD600:

600 g/m² area weight

Plain weave

Warp 0° -> 80% fibers

Weft 90° -> 20% fibers

Lay-up:

RGUD600 -> (x) = number of layers

(max. 8 layers = 4.0mm thickness)

Fibervolumecontent:

47% vol.

 

 

 

 

Glass/PA6

Tepex® dynalite 102-RG600(x)/47% black

Polymer:

PA6 black

Fiber RG600:

E-glass, 1200 tex

Weaving RG600:

600 g/m² area weight

Twill 2/2 binding

Warp 0° -> 50% fibers

Weft 90° -> 50% fibers

Lay-up:

RG600 -> (x) = number of layers

(max. 8 layers = 4.0mm thickness)

Fibervolumecontent:

47% vol.

 

Tepex® dynalite 102-RG601(x)/47% black

Polymer:

PA6.6 black

Fiber RG601:

E-glass, 1200 tex

Weaving RG601:

600 g/m² area weight

Plain weave

Warp 0° -> 50% fibers

Weft 90° -> 50% fibers

Lay-up:

RG601 -> (x) = number of layers

(max. 8 layers = 4.0mm thickness)

Fibervolumecontent:

47% vol.

 

Tepex® dynalite 102-RGUD600(x)/47% black

Polymer:

PA6 black

Fiber RGUD600:

E-glass, 1200 tex

Weaving RGUD600:

600 g/m² area weight

Plain weave

Warp 0° -> 80% fibers

Weft 90° -> 20% fibers

Lay-up:

RGUD600 -> (x) = number of layers

(max. 8 layers = 4.0mm thickness)

Fibervolumecontent:

47% vol.

 

 

Glass/PP

Tepex® dynalite 104-RG600(x)/47% black

Polymer:

PP black

Fiber RG600:

E-glass, 1200 tex

Weaving RG600:

600 g/m² area weight

Twill 2/2 binding

Warp 0° -> 50% fibers

Weft 90° -> 50% fibers

Lay-up:

RG600 -> (x) = number of layers

(max. 8 layers = 4.0mm thickness)

Fibervolumecontent:

47% vol.

 

Tepex® dynalite 104-RG601(x)/47% black

Polymer:

PP black

Fiber RG601:

E-glass, 1200 tex

Weaving RG601:

600 g/m² area weight

Plain weaving

Warp 0° -> 50% fibers

Weft 90° -> 50% fibers

Lay-up:

RG601 -> (x) = number of layers

(max. 8 layers = 4.0mm thickness)

Fibervolumecontent:

47% vol.

 

Tepex® dynalite 104-RGUD600(x)/47% black

Polymer:

PP black

Fiber RGUD600:

E-glass, 1200 tex

Weaving RGUD600:

600 g/m² area weight

Plain weaving

Warp 0° -> 80% fibers

Weft 90° -> 20% fibers

Lay-up:

RGUD600 -> (x) = number of layers

(max. 8 layers = 4.0mm thicknss)

Fibervolumecontent:

47% vol.

 

 

 