Many industrial processes and applications rely on efficient use of energy. Moving parts made of Tepex® can significantly reduce their kinetic energy through weight reduction without compromising structural performance.

Specific material properties like flame retardancy, resistance against elevated temperatures as well as the ability to absorb ballistic energy extend the field of applications for Tepex® in many industrial segments such as electrical and electronic equipment, in the public transport sector, protection sector or in the aerospace industry.

Major challenges in industrial applications can be addressed with Tepex® material solutions:

  • Weight reduction
  • Flame retardancy
  • Mass production ability

The following menu shows standard Tepex® materials for Industry applications. Custom made material lay-ups as well as special fabric constructions will be available on request.

GLASS/PA66

Tepex® dynalite 101-RG600(x)/47% black

Polymer:PA6.6 black
Fiber RG600:E-glass, 1200 tex
Weaving RG600:600 g/m² area weight
Twill 2/2 binding
Warp 0° -> 50% fibers
Weft 90° -> 50% fibers
Lay-up:RG600 -> (x) = number of layers
(max. 8 layers = 4.0mm thickness)
Fibervolumecontent:47% vol.

 

Tepex® dynalite 101-FG290(x)/45% black

Polymer:PA6.6 black
Fiber FG290:E-glass, 204 tex
Weaving FG290:290 g/m² area weight
Twill 2/2 binding
Warp 0° -> 50% fibers
Weft 90° -> 50% fibers
Lay-up:FG290 -> (x) = number of layers
(max. 8 layers = 2.0mm thickness)
Fibervolumecontent:45% vol.

 

 

 

CARBON/PA66

Tepex® dynalite 201-C200(x)/45%

Polymer:PA6.6 nature
Fiber C200:3K Carbon
Weaving C200:200 g/m² area weight
Twill 2/2 binding
Warp 0° -> 50% fibers
Weft 90° -> 50% fibers
Lay-up:C200 -> (x) = number of layers
(max. 12 layers = 3.0mm thickness)
Fibervolumecontent:45% vol.

 

 

 

CARBON-GLASS/PA66

Tepex® dynalite 401-C200(2)-FG290(x)/45%

Polymer:PA6.6 nature
Fiber outer layers (C200):3K Carbon
Fiber core (FG290):E-glass, 204 tex
Weaving C200:200 g/m² area weight
Twill 2/2 binding
Warp 0° -> 50% fibers
Weft 90° -> 50% fibers
Weaving FG290:290 g/m² area weight
Twill 2/2 binding
Warp 0° -> 50% fibers
Weft 90° -> 50% fibers
Lay-up:C200 -> 1 layer
FG290 -> (x) = number of layers (max. 10)
C200 -> 1 layer
Fibervolumecontent:45% vol.
A symmetric lay-up is mendatory. The number of glass fabric layers
can be adjusted individually. From 1 glass fabric layer (= 0.75mm total
thickness) up to 10 glass fabric layers (= 3.0mm total thickness).

 

 

 

GLASS/PPS

Tepex® dynalite 107-FG290(x)/45%

Polymer:PPS
Fiber FG290:E-glass, 204 tex
Weaving FG290:290 g/m² area weight
Twill 2/2 binding
Warp 0° -> 50% fibers
Weft 90° -> 50% fibers
Lay-up:FG290 -> (x) = number of layers
(max. 8 layers = 2.0mm thickness)
Fibervolumecontent:45% vol.

 

 

 

CARBON/PPS

Tepex® dynalite 207-C200(x)/45%

Polymer:PPS
Fiber C200:3K Carbon
Weaving C200:200 g/m² area weight
Twill 2/2 binding
Warp 0° -> 50% fibers
Weft 90° -> 50% fibers
Lay-up:C200 -> (x) = number of layers
(max. 8 layers = 2.0mm thickness)
Fibervolumecontent:45% vol.

 

 

 

CARBON-GLASS/PPS

Tepex® dynalite 407-C200(2)-FG290(x)/45%

Polymer:PPS
Fiber outer layers (C200):3K Carbon
Fiber core (FG290):E-glass, 204 tex
Weaving C200:200 g/m² area weight
Twill 2/2 binding
Warp 0° -> 50% fibers
Weft 90° -> 50% fibers
Weaving FG290:290 g/m² area weight
Twill 2/2 binding
Warp 0° -> 50% fibers
Weft 90° -> 50% fibers
Lay-up:C200 -> 1 layer
FG290 -> (x) = number of layers (max. 6)
C200 -> 1 layer
Fibervolumecontent:45% vol.
A symmetric lay-up is mendatory. The number of glass fabric layers can
be adjusted individually. From 1 glass fabric layer (= 0.75mm total
thickness) up to 6 glass fabric layers (= 2.0mm total thickness).